機械用石墨特性
首頁 > 材料>機械用石墨特性機械用途
| 組成 | 材質 | 體積密度 | 硬度 | 彎曲強度 | 壓縮強度 | 楊氏模數 | 熱膨脹係數 | 熱傳導率 | 耐熱溫度 |
| Mg/m3 | (HSD) | MPa | MPa | GPa | 10-6/K | W/(m･K) | ℃ | ||
| 黑鉛質 | IG-11 | 1.77 | 51 | 39 | 78 | 10 | 4.5 a) | 120 | 450 |
| ISO-68 | 1.82 | 80 | 76 | 172 | 13 | 5.6 a) | 70 | 450 | |
| KC-878 ** | 1.92 | 105 | 100 | 230 | 17 | 5.5 a) | 40 | 400 | |
| IKC-88 | 1.88 | 95 | 110 | 220 | 17 | 5.5 a) | 40 | 400 | |
| 炭素黑鉛質 | KC-36 | 1.72 | 65 | 48 | 135 | 15 | 3.5 | 15 | 350 |
| KC-57 | 1.78 | 105 | 70 | 270 | 20 | 4 | 5 | 350 | |
| KC-67 | 1.77 | 72 | 60 | 185 | 20 | 3.5 | 10 | 350 | |
| KC-83K | 1.74 | 80 | 55 | 160 | 15 | 4 | 10 | 350 | |
| 樹脂含浸質 | KC-360 | 1.78 | 75 | 58 | 165 | 17 | 4 | 15 | 300 |
| KC-570 * | 1.85 | 110 | 84 | 370 | 22 | 5 | 5 | 300 | |
| KC-573 * | 1.85 | 110 | 85 | 370 | 22 | 5.5 | 5 | 250 | |
| KC-670 * | 1.87 | 87 | 78 | 240 | 22 | 5 | 10 | 300 | |
| KC-673 * | 1.87 | 87 | 78 | 245 | 22 | 5.5 | 10 | 250 | |
| KC-830K | 1.84 | 90 | 70 | 205 | 17 | 5 | 10 | 250 | |
| 金屬含浸質 | KC-5709 * | 2.25 | 110 | 100 | 430 | 27 | 5 | 5 | 500 |
| KC-6707 * | 2.35 | 80 | 73 | 240 | 25 | 5 | 13 | 250 | |
| KC-6709 * | 2.3 | 88 | 90 | 300 | 27 | 5 | 13 | 500 | |
| IKC-6809 | 2.67 | 88 | 105 | 300 | 21 | 6 | 80 | 500 | |
| PC-78 | 3 | 95 | 120 | 440 | 30 | 6.5 | 10 | 350 | |
| PC-78A | 2.9 | 95 | 110 | 410 | 27 | 6.5 | 13 | 350 | |
| SiC/C複合質 | TS-002 | 2.31/2.75 | 63/70 | 113/78 | 300/205 | 18/16 | 4.5/5.2 | 80/80 | 500 |
| TS-003 | 2.31/1.82 | 80/80 | 125/76 | 405/170 | 30/13 | 5.4/5.6 | 70/70 | 400 | |
| TS-004 | 2.31/1.92 | 81/86 | 124/88 | 415/235 | 30/15 | 5.4/7.5 | 70/60 | 200 | |
| TS-005 | 2.28/2.67 | 83/90 | 116/109 | 410/295 | 30/21 | 5.4/6.0 | 70/70 | 500 | |
| 無機物含浸質 | IG-11R1 | 1.85 | 55 | 46 | 92 | 11 | 5.5 | 120 | 500 |
| ISO-68R1 | 1.87 | 84 | 83 | 190 | 15 | 5 | 70 | 500 | |
| B4C/C 複合質 | GB-010 | 1.87 | 86 | 77 | 190 | 23 | 5 | 30 | 800 |
| GB-210 | 1.85 | 82 | 72 | 175 | 20 | 5 | 30 | 800 | |
|
不浸透性炭素 黑鉛質 |
TUG-105 | 1.67 | 90 | 60 | 250 | 20 | 4 | - | 350 |
| TUG-110 | 1.78 | 105 | 90 | 290 | 20 | 4 | - | 350 | |
| TUG-120 | 1.68 | 95 | 70 | 245 | 20 | 4 | - | 350 | |
| TUG-307 | 1.91 | 90 | 75 | 235 | 25 | 3.5 | - | 350 | |
| TUG-308 | 1.87 | 90 | 65 | 215 | 23 | 3.5 | - | 350 | |
| TUG-309 | 1.85 | 80 | 55 | 185 | 20 | 3.5 | - | 350 | |
| TUG-3095 | 1.81 | 75 | 50 | 170 | 20 | 3.5 | - | 350 | |
| TUG-505 | 1.89 | 80 | 68 | 185 | 20 | 3 | - | 350 | |
| 樹脂結合質 | W-1500 | 1.77 | 70 | 75 | 175 | 15 | 23.0 b) | - | 150 |
| W-3500* | 1.63 | 85 | 90 | 250 | 12 | 30.0 b) | - | 200 | |
| LS | 1.77 | 60 | 70 | 100 | 15 | 15.0 b) | - | 150 | |
| NLA | 1.7 | 75 | 85 | 175 | 15 | 23.0 b) | - | 150 | |
| MR-10* | 1.43 | 78 | 100 | 230 | 10 | 35.0 b) | - | 220 | |
| 金屬結合質 | GM-1 | 4.6 | 18 | 25 | 55 | - | 12 | - | 200 |
| GM-5 | 6.2 | 18 | 205 | 350 | - | 12 | - | 400 |
*專利申請中
**專利號2635996
表中的數字乃特性代表值, 而非保證值.
SiC/C複合材的特性值, 是同時表示"SiC/C複合層部分"和"塊材(+含浸)"這2者的數值.
SiC/C複合材的耐熱溫度, 是以"塊材(+含浸)"的數值來表示.
熱膨脹係數的量測溫度範圍為 a) 350 to 450℃ b) 50 to 150℃ 其他 : 100 ~ 200℃.
單位換算 : MPa=kgf/cm2×0.098、 GPa=kgf/mm2×0.0098、 W/(m･K)=kcal/h･m・℃ ×1.16